Typical Properties of HPMS PAN Based Carbon Felt & Graphite Felt

Properties
 Carbon Felt
 Graphite Felt
Bulk density (g/cm3)
 0.14
 0.10
Carbon content (%)
 98.5
 > 99.5
Ash content (%)
 < 0.75
 0.05
Thermal conductivity (W/mk)
(at 1500 °C)
 0.13
 0.08
Tensile strength
(MPa)
 0.18
 0.12
Min. Process Temperature
(°C)
 1500
 2400
Thickness (mm)
 3, 5, 8, 10, 12
 5, 8, 10, 12
Width (mm)
 1000 - 1300
 1000 - 1300
Length (m)
 9 - 12
 9 - 12
Carbon felt and graphite felt are designed  for
use  as  high  temperature insulation in
vacuum furnaces and inert gas furnaces. The
needle-punched PAN based carbon and
graphite felt is light in weight and has low
thermal conductivity. It can be used in
oxidizing temperatures up to 400 °C and in
vacuum or protective atmospheres up to 3200
°C

Carbon Felt & Graphite Felt
Home  |  About Us  |  Activated Carbon Fiber  |  Graphite Foil  |  Flake Graphite  |  Graphite Yarn  |  Contact Us

HP Materials Solutions, Inc.
5850 Canoga Ave, #400, Woodland Hills,  CA 91367, USA    
Tel: 1-888-375-1803  |  Fax: 818-360-4489  |  E-mail: support@hpmsgraphite.com              

Typical Properties of HPMS Rayon Based Carbon Felt & Graphite Felt

Properties
 Carbon Felt (Grade HCF)
 Graphite Felt (Grade HGF)
Bulk density (g/cm3)
0.09 - 0.10
0.08
Carbon content (%)
≥ 99
≥ 99.9
Ash content (%)
≤ 0.05
≤ 0.01
Thermal conductivity (W/mk)
(at 1500 °C)
0.22
0.39
Sublimation Temperature (°C)
3600
3600
Tensile strength
(MPa)
0.13
0.10
Min. Process Temperature
(°C)
1400
2200-2500
Thickness (mm)
3, 5, 8, 10, 12
5, 8, 10, 12
Width (mm)
1000 - 1300
1000 - 1300
Length (m)
9 - 12
9 - 12